Cyclic　deformation　behavior　of　Ti-5　at.%　Al　single　crystals　subjected　to　pull-push　cyclic　load　along　[0　0　0　1]　crystallographic　orientation　was　studied.　A　higher　cyclic　stress　response　was　displayed　in　the　Ti-5Al　single　crystal　oriented　for　[0　0　0　1]　than　that　oriented　for　single　prism　slip.　Optical　microscopy　and　transmission　electron　microscopy　examinations　show　that　twinning　is　a　dominant　plastic　deformation　mode　in　the　single　crystals　during　cycling.　Trace　analysis　of　prepolished　surfaces　was　used　to　identify　the　twin　systems　primarily　responsible　for　deformation.　The　major　twin　type　observed　was　{1　0　(1)　over　bar　2},　{1　1　(2)　over　bar　2},　{1　0　(1)　over　bar　1}　and　{1　1　(2)　over　bar　1}.　＜　c　+　a　＞　slip　was　observed　in　the　neighboring　region　of　twins　in　the　fatigued　specimens.　The　activation　of　multiple　twinning　systems　contributed　to　the　higher　cyclic　saturation　stress　in　Ti-5Al　single　crystals　oriented　for　[0　0　0　1].　(c)　2004　Elsevier　B.V.　All　rights　reserved.