Ti-modified　thin　films　of　multiferroic　0.72Bi(Fe1-xTix)O-3-0.28PbTiO(3)　(BFPT,　x　=　0　and　0.02)　solid　solution　were　prepared　by　pulsed　laser　deposition.　The　BFPT　(x　=　0　and　0.02)　films　possess　a　tetragonal　structure　with　highly　preferential　(001)　orientation.　The　effects　of　the　ionic　substitution　on　the　Properties　of　BFPT　(x　=　0　and　0.02)　films　have　been　investigated.　The　leakage　current　of　the　BFPT　(x　=　0.02)　thin　film　is　significantly　reduced,　and　the　dielectric　and　ferroelectric　properties　greatly　improved　by　the　aliovalent　ionic　substitution　of　Ti4+　for　Fe3+.　The　BFPT　(x　=　0.02)　thin　film　exhibits　a　reasonably　high　remnant　polarization　P-r　with　2P(r)　up　to　go　mu　C/cm(2)　at　312　kV/cm　and　a　switchable　polarization　up　to　92　mu　C/cm(2)　at　417　kV/cm.　(C)　2009　Elsevier　B.V.　All　rights　reserved.