Characteristics　and　life　expression　of　fatigue　fracture　of　drill　pipe　steels　for　API　G105　and　S135　grade　were　investigated　experimentally.　S135　steel　with　higher　tensile　strength　has　higher　fatigue　strength　and　fatigue　limit　than　that　of　G105　steel　with　lower　tensile　strength.　A　modified　model　for　the　S-N　data,　revealing　the　correlation　between　the　fatigue　life　and　fatigue　limit,　equivalent　stress　amplitude　reflecting　the　effect　of　stress　ratio,　is　suggested　for　predicting　the　fatigue　damage.　The　fatigue　limit　and　the　fatigue　strength　coefficient　are　correlated　to　the　tensile　properties.　The　mechanism　of　the　fatigue　fracture　was　examined　by　scanning　electron　microscopy.　©　2020　Elsevier　Ltd