A　liquid　feedstock　flame　spraying　system　was　developed　to　deposit　the　nanostructured　TiO2　coating　using　butyl　titanate　(Ti(OC4H9)(4))　and　ethanol　solution　as　precursor.　The　resultant　deposit　was　characterized　by　infrared　spectrum　(IR),　X-ray　diffraction　(XRD),　scanning　electron　microscopy　(SEM)　and　transmission　electron　microscopy　(TEM).　The　results　showed　that　during　spraying,　butyl　titanate　had　been　completely　decomposed　and　converted　into　nanostructured　anatase　TiO2,　having　a　narrow　size　distribution　from　10　to　20　nm.　(C)　2002　Elsevier　Science　B.V.　All　rights　reserved.