Du, Xianfeng (Du, Xianfeng.) | Xu, Youlong (Xu, Youlong.)

Indexed by:

SCIE

Abstract:

To increase the specific capacitance of aluminum anodic foil, barium titanate BaTiO3 (BT) sol was dip-coated on the etched aluminum foils by a sol-gel process. After annealed at different temperatures, the foils were anodized in ammonium adipate solution. The phase transition of BT powder was investigated. The voltage-time variations during anodizing were monitored, and the electric properties such as specific capacitance, dissipation factor, withstanding voltage, and leakage current of these foils were also examined. It was found that BT started to crystallize at 550 degrees C. The anodizing time of the foils covered with BT films decreased with annealing temperature. The specific capacitance and the product of specific capacitance and withstanding voltage of anodic foils with a BT coating increased with annealing temperature, and the largest increases were about 46% and 39% compared to that without a BT coating, respectively. The obtained anodic foils with the largest specific capacitance were assembled into aluminum electrolytic capacitors, and the load and shelf life tests were measured. There was no significant difference between Al/BT-600 and Al during the load and shelf life tests. The capacitor life time is larger than 2500h. From the results, BaTiO3 is promising to be used as the partial dielectric of aluminum electrolytic capacitor to increase the specific capacitance. (C) 2008 Elsevier B.V. All rights reserved.

Keyword:

Aluminum electrolytic capacitor Barium titanate Load and shelf life Sol-gel

Author Community:

  • [ 1 ] [Du, Xianfeng; Xu, Youlong] Xian Jiaotong Univ, Minist Educ, Key Lab, Elect Mat Res Lab, Xian 710049, Peoples R China

Reprint Author's Address:

  • Xian Jiaotong Univ, Minist Educ, Key Lab, Elect Mat Res Lab, Xian 710049, Peoples R China.

Show more details

Related Keywords:

Source :

THIN SOLID FILMS

ISSN: 0040-6090

Year: 2008

Issue: 23

Volume: 516

Page: 8436-8440

1 . 8 8 4

JCR@2008

2 . 1 8 3

JCR@2020

ESI Discipline: MATERIALS SCIENCE;

JCR Journal Grade:2

CAS Journal Grade:3

Cited Count:

WoS CC Cited Count: 26

SCOPUS Cited Count: 34

ESI Highly Cited Papers on the List: 0 Unfold All

WanFang Cited Count:

Chinese Cited Count:

30 Days PV: 11

FAQ| About| Online/Total:666/199563425
Address:XI'AN JIAOTONG UNIVERSITY LIBRARY(No.28, Xianning West Road, Xi'an, Shaanxi Post Code:710049) Contact Us:029-82667865
Copyright:XI'AN JIAOTONG UNIVERSITY LIBRARY Technical Support:Beijing Aegean Software Co., Ltd.